以下列出擠出從Xtel XE版系列化合物管一般加工建議Xtel PPS系列化合物（Xtel 聚苯硫醚）。

Extruder Set-Up
• 24:1 to 28:1 L/D
• General Purpose screw with 2.5:1 to 3:1
Compression ratio. Mixing head optional.
• 20/80/20 Screenpack
• Heated Die Clamp
Pipe Die
• Low volume, high compression die head
suitable for low melt viscosity materials
• Die bushing ID should be 1.3 to 1.7 times
the pipe diameter
• Die annulus 1.6 to 2.0 times the desired
pipe wall thickness
Sizing
• Aluminum sleeve designed for low
vacuum sizing (1.5 mm diameter holes,
not slotted)
Pipe Extrusion Line Schematic
•    Sleeve diameter for 1% to 2% shrinkage
•    Multiple sectioned tank with short vacuum section.
Material Drying
• Dry at 275°F to 300°F (135°C to 150°C)
for 2 hours prior to processing
• Hopper driers and/or desiccant driers are
not required
Temperature Profile for 3:1 Screw
  Extruder Zone 1  550°F  (288°C)
  Extruder Zone 2  570°F  (300°C)
  Extruder Zone 3  570°F  (300°C)
  Extruder Zone 4  570°F  (300°C)
  Adaptor 570°F  (300°C)
  Die 1 560°F  (293°C)
  Die 2 560°F  (293°C)

Xtel PPS需要足夠的加熱時(shí)間,啟動(dòng)擠出機(jī)至關(guān)重要的是確保穩(wěn)定加工的溫度。如果溫度不夠擠出將造成的阻塞。 Xtel  XE系列化合物（Xtel PPS）過程更擠出率較高的地方是從螺桿融化而不是加熱器。擠出機(jī)應(yīng)調(diào)整到高于50％的過程中運(yùn)行的溫度，同時(shí)盡量減少停留時(shí)間。皂泡，煙霧或凝膠都是在擠出機(jī)里過于熱，時(shí)間太久而造成的。溫度適當(dāng)調(diào)整，但模具不低于540華氏度（282℃）設(shè)置。如果需要熔體溫度降低，選的調(diào)整擠出機(jī)的溫度分布，而不是降低模具溫度。持續(xù)融化以上600 °F對(duì)于長(zhǎng)期的時(shí)間段（315℃）的溫度會(huì)導(dǎo)致材料熱降解的結(jié)果。

如有疑問可繼續(xù)瀏覽更多Xtel PPS加工指南或聯(lián)絡(luò)我公司客戶服務(wù)中心索取該資料.